Hydroxy-functional polyether-based reaction products and aqueous base paint which contains the reaction products

ABSTRACT

Provided herein is a pigmented aqueous basecoat material including a hydroxy-functional polyether-based reaction product that is prepared by a urethane group-forming reaction of:
         (a) at least one component including isocyanate groups that is prepared by the urethane group-forming reaction of at least one organic diisocyanate (a1) with at least one polyether (a2) of the general structural formula (I).       

     
       
         
         
             
             
         
       
     
     R is a C 3  to C 6  alkylene radical, and n is selected accordingly such that a polyether (b) possesses a number-average molecular weight of 500 to 5000 g/mol,
 
the components (a1) and (a2) being used in a molar ratio of 1.8/1.7 to 3.0/1.0, and the resulting component (a) having an isocyanate content of 0.5 to 10.0% with (b) at least one organic polyol.

The present invention relates to innovative hydroxy-functional,polyether-based reaction products. It further relates to aqueousbasecoat materials which comprise the reaction products and also to theuse of said reaction products in aqueous basecoat materials. Itadditionally relates to a method for producing multicoat paint systemsusing aqueous basecoat materials, and also to the multicoat paintsystems producible by means of said method.

PRIOR ART

There are a multiplicity of known methods for producing multicoat colorand/or effect paint systems (also called multicoat finishes). The priorart (compare, for example, German patent application DE 199 48 004 A1,page 17, line 37, to page 19, line 22, or German patent DE 100 43 405C1, column 3, paragraph [0018], and column 8, paragraph [0052], column9, paragraph [0057], in conjunction with column 6, paragraph [0039], tocolumn 8, paragraph [0050]), for example, discloses the followingmethod, which involves

-   (1) applying a pigmented aqueous basecoat material to a substrate,-   (2) forming a polymer film from the coating material applied in    stage (1),-   (3) applying a clearcoat material to the resultant basecoat, and    subsequently-   (4) curing the basecoat together with the clearcoat.

This method is widely used, for example, for the original finish (OEM)of automobiles and also for the painting of metal and plastic parts forinstallation in or on vehicles. The present-day requirements for thetechnological qualities of such paint systems (coatings) in applicationare massive.

A constantly recurring problem and one still not resolved to completesatisfaction by the prior art is the mechanical resistance of themulticoat systems produced, particularly with respect to stonechipeffects.

The qualities of the basecoat material, which is particularly importantin this context, and of the coats produced from it are determined inparticular by the binders and additives—for example, specific reactionproducts—present in the basecoat material.

A further factor is that nowadays the replacement of coatingcompositions based on organic solvents by aqueous coating compositionsis becoming ever more important, in order to meet the risingrequirements for environmental compatibility.

Problem

The problem addressed by the present invention was therefore that ofproviding a reaction product which can be used to produce coatings thatno longer have the disadvantages referred to above in the prior art.More particularly, the provision of a new reaction product and the usethereof in aqueous basecoat materials ought to create the opportunityfor provision of coatings which exhibit outstanding adhesion qualitiesand very good stonechip resistance and which at the same time can beproduced in an eco-friendly way through the use precisely of aqueousbasecoat materials.

Solution

The problems stated have been solved by a pigmented aqueous basecoatmaterial which comprises a hydroxy-functional, polyether-based reactionproduct which is preparable by reaction of

(a) at least one component containing isocyanate groups which ispreparable by urethane group-forming reaction of at least one organicdiisocyanate (a1) with at least one polyether (a2) of the generalstructural formula (I)

in whichR is a C₃ to C₆ alkylene radical and n is selected accordingly such thatthe polyether (b) possesses a number-average molecular weight of 500 to5000 g/mol,the components (a1) and (a2) being used in a molar ratio of 1.8/1.7 to3.0/1.0 and the resulting component (a) having an isocyanate content of0.5 to 10.0%with(b) at least one organic polyol,where the amounts of components (a) and (b) are harmonized with oneanother such that the ratio of the molar amount of isocyanate groups incomponent (a) to the molar amount of component (b) is in a range from0.33 to 0.95 and the resulting reaction product has a number-averagemolecular weight of 700 to 20 000 g/mol.

The condition that n is selected such that said polyether possesses anumber-average molecular weight of 500 to 5000 g/mol may be illustratedas follows: Where, for example, R is a tetramethylene radical and thenumber-average molecular weight is to be 1000 g/mol, n is on averagebetween 13 and 14. From the mandates given, the skilled person is wellaware of how to produce or select a corresponding reaction product.Apart from this, the description below, and particularly the examples,further provide additional information. The parameter n is therefore tobe understood as a statistical average value, just like thenumber-average molecular weight.

The new basecoat material is also referred to below as basecoat materialof the invention. Preferred embodiments of the basecoat material of theinvention are apparent from the following description and also from thedependent claims.

Likewise provided for the present invention is the reaction product perse and also the use of the reaction product in aqueous basecoatmaterials for improving the stonechip resistance. The present inventionrelates not least to a method for producing a multicoat paint system ona substrate and also to a multicoat system produced by the statedmethod.

Through the use of the reaction products of the invention, basecoatmaterials are obtained whose use in the context of production ofcoatings, especially multicoat paint systems, leads to very goodstonechip resistance. The reaction product of the invention and also thebasecoat material of the invention can be used in the area of originalfinishing, particularly in the automobile industry sector, and in thearea of automotive refinish.

Component (a)

The reaction product of the invention is preparable using at least onespecific component containing isocyanate groups. The componentcontaining isocyanate groups is preparable by urethane group-formingreaction of at least one organic diisocyanate (a1) with at least onespecific hydroxy-functional polyether (a2). Components (a1) and (a2) areused here in a molar ratio of 1.8/1.7 to 3.0/1.0, preferably of 1.8/1.6to 2.5/1.0, more preferably 1.8/1.5 to 2.2/1.0. The organic diisocyanate(a1), accordingly, is used in a molar excess relative to the polyether(a2). This is in turn synonymous with the fact that component (a)contains isocyanate groups.

Where, for example, one molar equivalent of polyether (a2) is reactedwith two molar equivalents of diisocyanate (a1), the result on average,and within intrinsic experimental margins of error, a blocklike productof the form A-B-A may result, where A stands for the reacteddiisocyanate and B for the reacted polyether. Here, the two constituentsA each contain an unreacted isocyanate group. Moreover, the productA-B-A has two bridging groups, namely urethane groups. The actualcircumstances, which optionally deviate on the basis of experimentalerrors, may be simply found by taking account of the molecular weightsof the starting compounds and undertaking comparison with the measurednumber-average molecular weight of component (a) and/or with theisocyanate content of component (a).

Where two molar equivalents of polyether (a2) are reacted with threemolar equivalents of diisocyanate (a1), on average a blocklike productof the form A-B-A-B-A may result. Component (a) may therefore bedescribed theoretically or on average, and not accounting forexperimental deviations, by the formula A-(B-A)_(m). The parameter m inthis case represents a statistical mean value which of course, dependingon the ratios of the starting compounds that are used, may also adoptuneven values. The skilled person is able to adapt the molar ratioswithout problems.

Also known are the underlying reaction mechanisms and reactionconditions for achieving linking of the hydroxyl groups with theisocyanate groups.

As organic diisocyanates (a1) it is possible to use the diisocyanatesthat are known per se, examples being hexamethylene diisocyanate,octamethylene diisocyanate, decamethylene diisocyanate, dodecamethylenediisocyanate, tetradecamethylene diisocyanate, trimethylhexanediisocyanate, tetramethylhexane diisocyanate, isophorone diisocyanate(IPDI), 2-isocyanatopropylcyclohexyl isocyanate, dicyclohexylmethane2,4′-diisocyanate, dicyclohexylmethane 4,4′-diisocyanate, 1,4- or1,3-bis(isocyanatomethyl)-cyclohexane, 1,4- or 1,3- or1,2-diisocyanatocyclo-hexane, 2,4- or2,6-diisocyanato-1-methylcyclohexane, meta-tetramethylxylenediisocyanate (TMXDI), and mixtures of these polyisocyanates. Preferredfor use is IPDI.

The hydroxy-functional polyether (a2) may be described by the followinggeneral structural formula (I):

where R is a C₃ to C₆ alkyl radical and where the index n should beselected in each case such that said polyether possesses anumber-average molecular weight of 500 to 5000 g/mol. With preference itpossesses a number-average molecular weight of 500 to 4000 g/mol, morepreferably of 550 to 3500 g/mol, and very preferably from 600 to 3200g/mol. The number-average molecular weight may for example be 1000g/mol, 2000 g/mol, or 3000 g/mol.

In the polyether (a2), all n radicals R may be the same. It is alsopossible, though, for different kinds of radicals R to be present.Preferably all the radicals R are the same.

R is preferably a C₄ alkylene radical. More preferably it is atetramethylene radical.

With very particular preference the polyether (a2) is a linearpolytetrahydrofuran which on average is diolic.

The isocyanate content of component (a) is from 0.5 to 10.0%. Preferablyit is from 1.0 to 6.5%.

Component (b)

The reaction products of the invention can be prepared using at leastone organic polyol. Suitable organic polyols ultimately include allorganic monomeric compounds having at least 2 hydroxyl groups that areknown in this context to the skilled person. Preferred are organicpolyols having 2 to 6, more preferably 2 to 3, hydroxyl groups permolecule.

Suitable diols are, for example, glycols, such as ethylene glycol,propylene glycol, butylene glycol, 1,4-butanediol, 1,6-hexanediol,neopentyl glycol, and other diols, such as 1,4-dimethylolcyclohexane or2-butyl-2-ethyl-1,3-propanediol. Suitable polyols of higherfunctionality (OH functionality more than 2) are, for example,trimethylolpropane, glycerol, penta-erythritol, and sorbitol.

Preferred organic polyols used are those having at least 3 hydroxylgroups, preferably exactly 3 hydroxyl groups. An especially preferredorganic polyol is trimethylolpropane.

The Reaction Product

There are no peculiarities to the preparation of the reaction product.The components (a) and (b) are linked with one another viacommon-knowledge urethane-forming reactions of hydroxyl groups withisocyanate groups. The reaction may take place, for example, in bulk orin solution with typical organic solvents at temperatures of 50° C. to150° C., for example. Use may of course also be made of typicalcatalysts such as sulfuric acid, sulfonic acids and/or tetraalkyltitanates, zinc and/or tin alkoxylates, dialkyltin oxides such asdi-n-butyltin oxide, for example, or organic salts of the dialkyltinoxides. The reaction conditions specified here may of course also beemployed in the reaction, analogous in this respect, of theabove-described components (a1) and (a2).

The amounts of components (a) and (b) here are harmonized with oneanother in such a way that the ratio of the molar amount of isocyanategroups in component (a) to the molar amount of component (b) is in arange from 0.33 to 0.95 and the resulting reaction product has anumber-average molecular weight of 700 to 20 000 g/mol. Preferably theratio is in the range from 0.40 to 0.85 and very preferably in the ratioof 0.45 to 0.75. The molar amount of isocyanate groups here may bedetermined easily from the afore-determined NCO content of component(a).

The resulting reaction product possesses preferably a number-averagemolecular weight of 1000 to 15 000 g/mol, more preferably of 1500 to 12000 g/mol, and very preferably of 1800 to 10 000 g/mol.

As a result of the fact that a molar excess of component (b) in relationto the isocyanate groups is used in the reaction described above, andcomponent (b) has at least two hydroxyl groups, the resulting reactionproduct is a hydroxy-functional reaction product.

For especially preferred reaction products it is the case that they arepreparable by reaction of a component (a) having an isocyanate contentof 1.0 to 6.5% with (b) trimethylolpropane, the amounts of components(a) and (b) being harmonized with one another in such a way that theratio of the molar amount of isocyanate groups in component (a) to themolar amount of component (b) is in a range from 0.45 to 0.75 and theresulting reaction product has a number-average molecular weight of 1500to 12 000 g/mol.

The Pigmented Aqueous Basecoat Material

The present invention relates further to a pigmented aqueous basecoatmaterial which comprises at least one reaction product of the invention.All of the above-stated preferred embodiments in relation to thereaction product also apply, of course, to the basecoat materialcomprising the reaction product.

A basecoat material is understood to be a color-imparting intermediatecoating material that is used in automotive finishing and generalindustrial painting. This basecoat material is generally applied to ametallic or plastics substrate which has been pretreated with a baked(fully cured) surfacer or primer-surfacer, or else, occasionally, isapplied directly to the plastics substrate. Substrates used may alsoinclude existing paint systems, which may optionally requirepretreatment as well (by abrading, for example). It has now becomeentirely customary to apply more than one basecoat film. Accordingly, insuch a case, a first basecoat film constitutes the substrate for asecond such film. A particular possibility in this context, instead ofapplication to a coat of a baked surfacer, is to apply the firstbasecoat material directly to a metal substrate provided with a curedelectrocoat, and to apply the second basecoat material directly to thefirst basecoat film, without separately curing the latter. To protect abasecoat film, or the uppermost basecoat film, from environmentaleffects in particular, at least an additional clearcoat film is appliedover it. This is generally done in a wet-on-wet process—that is, theclearcoat material is applied without the basecoat film(s) being cured.Curing then takes place, finally, jointly. It is now also widespreadpractice to produce only one basecoat film on a cured electrocoat film,then to apply a clearcoat material, and then to cure these two filmsjointly. The latter is a preferred embodiment in the context of thepresent invention. The reason is that when using the reaction product ofthe invention, in spite of the production of only one basecoat andtherefore of a consequent significant simplification in operation, theresult is excellent stonechip resistance.

The sum total of the weight-percentage fractions, based on the totalweight of the pigmented aqueous basecoat material, of all reactionproducts of the invention is preferably 0.1 to 20 wt %, more preferably0.5 to 15 wt %, and very preferably 1.0 to 10 wt % or even 1.5 to 5 wt%.

Where the amount of the reaction product of the invention is below 0.1wt %, it may be possible that no further improvement in adhesion andstonechip resistance is achieved. Where the amount is more than 20 wt %,there may in certain circumstances be disadvantages, on account of thethen numerous potentially polar groups (hydroxyl groups) in the reactionproduct, in terms of the condensation resistance of the paint systemproduced from the basecoat material.

In the case of a possible particularization to basecoat materialscomprising preferred reaction products in a specific proportional range,the following applies. The reaction products which do not fall withinthe preferred group may of course still be present in the basecoatmaterial. In that case the specific proportional range applies only tothe preferred group of reaction products. It is preferred nonethelessfor the total proportion of reaction products, consisting of reactionproducts of the preferred group and reaction products which are not partof the preferred group, to be subject likewise to the specificproportional range.

In the case of restriction to a proportional range of 0.5 to 15 wt % andto a preferred group of reaction products, therefore, this proportionalrange evidently applies initially only to the preferred group ofreaction products. In that case, however, it would be preferable forthere to be likewise from 0.5 to 15 wt % in total present of alloriginally encompassed reaction products, consisting of reactionproducts from the preferred group and reaction products which do notform part of the preferred group. If, therefore, 5 wt % of reactionproducts of the preferred group are used, not more than 10 wt % of thereaction products of the nonpreferred group may be used.

The stated principle is valid, for the purposes of the presentinvention, for all stated components of the basecoat material and fortheir proportional ranges—for example, for the pigments, for thepolyurethane resins as binders, or else for the crosslinking agents suchas melamine resins (also known as melamine-formaldehyde resins).

The basecoat materials used in accordance with the invention comprisecolor and/or effect pigments. Such color pigments and effect pigmentsare known to those skilled in the art and are described, for example, inRömpp-Lexikon Lacke und Druckfarben, Georg Thieme Verlag, Stuttgart, NewYork, 1998, pages 176 and 451. The fraction of the pigments may besituated for example in the range from 1 to 40 wt %, preferably 2 to 35wt %, more preferably 3 to 30 wt %, based on the total weight of thepigmented aqueous basecoat material.

Preferred basecoat materials in the context of the present invention arethose which comprise, as binders, polymers curable physically,thermally, or both thermally and with actinic radiation. A “binder” inthe context of the present invention and in accordance with relevant DINEN ISO 4618 is the nonvolatile component of a coating composition,without pigments and fillers. Specific binders, accordingly, include,for example, typical coatings additives, the reaction product of theinvention, or typical crosslinking agents described later on below, evenif the expression is used primarily below in relation to particularpolymers curable physically, thermally, or both thermally and withactinic radiation, as for example particular polyurethane resins.

Besides the reaction product of the invention, the pigmented aqueousbasecoat materials of the invention more preferably comprise at leastone further polymer, different from the reaction product, as binder,more particularly at least one polymer selected from the groupconsisting of polyurethanes, polyesters, poly(meth)acrylates and/orcopolymers of the stated polymers, especially preferably at any rate,though not necessarily exclusively, at least onepolyurethane-poly(meth)acrylate.

In the context of the present invention, the term “physical curing”means the formation of a film through loss of solvents from polymersolutions or polymer dispersions. Typically, no crosslinking agents arenecessary for this curing.

In the context of the present invention, the term “thermal curing” meansthe heat-initiated crosslinking of a coating film, with either aseparate crosslinking agent or else self-crosslinking binders beingemployed in the parent coating material. The crosslinking agent containsreactive functional groups which are complementary to the reactivefunctional groups present in the binders. This is commonly referred toby those in the art as external crosslinking. Where the complementaryreactive functional groups or autoreactive functional groups—that is,groups which react with groups of the same kind—are already present inthe binder molecules, the binders present are self-crosslinking.Examples of suitable complementary reactive functional groups andautoreactive functional groups are known from German patent applicationDE 199 30 665 A1, page 7 line 28 to page 9 line 24.

For the purposes of the present invention, actinic radiation meanselectromagnetic radiation such as near infrared (NIR), UV radiation,more particularly UV radiation, and particulate radiation such aselectron radiation. Curing by UV radiation is commonly initiated byradical or cationic photoinitiators. Where thermal curing and curingwith actinic light are employed in unison, the term “dual cure” is alsoused.

In the present invention preference is given both to basecoat materialswhich are curable physically and to those which are curable thermally.In the case of basecoat materials which are curable thermally, there isof course always also a proportion of physical curing. For reasons notleast of ease of comprehension, however, these coating materials arereferred to as thermally curable.

Preferred thermally curing basecoat materials are those which compriseas binder a polyurethane resin and/or polyurethane-poly(meth)acrylate,preferably a hydroxyl-containing polyurethane resin and/orpolyurethane-poly(meth)acrylate, and as crosslinking agent an aminoplastresin or a blocked or nonblocked polyisocyanate, preferably anaminoplast resin. Among the aminoplast resins, melamine resins arepreferred.

The sum total of the weight-percentage fractions, based on the totalweight of the pigmented aqueous basecoat material, of all crosslinkingagents, preferably aminoplast resins and/or blocked and/or nonblockedpolyisocyanates, more particularly preferably melamine resins, ispreferably 1 to 20 wt %, more preferably 1.5 to 17.5 wt %, and verypreferably 2 to 15 wt % or even 2.5 to 10 wt %.

The polyurethane resin preferably present may be ionically and/ornonionically hydrophilically stabilized. In preferred embodiments of thepresent invention the polyurethane resin is ionically hydrophilicallystabilized. The preferred polyurethane resins are linear or containinstances of branching. The polyurethane resin is more preferably one inwhose presence olefinically unsaturated monomers have been polymerized.This polyurethane resin may be present alongside the polymer originatingfrom the polymerization of the olefinically unsaturated monomers,without these polymers being bonded covalently to one another. Equally,however, the polyurethane resin may also be bonded covalently to thepolymer originating from the polymerization of the olefinicallyunsaturated monomers. Both groups of the aforementioned resins, then,are copolymers, which in the case of the use of(meth)acrylate-group-containing monomers as olefinically unsaturatedmonomers, can also be called polyurethane-poly(meth)acrylates (see alsoearlier on above). This kind of polyurethane-poly(meth)acrylates areparticularly preferred for use in the context of the present invention.The olefinically unsaturated monomers are thus preferably monomerscontaining (meth)acrylate groups. It is likewise preferred for themonomers containing (meth)acrylate groups to be used in combination withother olefinically unsaturated compounds which contain no (meth)acrylategroups. Olefinically unsaturated monomers bonded covalently to thepolyurethane resin are more preferably monomers containing acrylategroups or (meth)acrylate groups. This form ofpolyurethane-poly(meth)acrylates is further preferred.

Suitable saturated or unsaturated polyurethane resins and/orpolyurethane-poly(meth)acrylates are described, for example, in

-   -   German patent application DE 199 14 896 A1, column 1, lines 29        to 49 and column 4, line 23 to column 11, line 5,    -   German patent application DE 199 48 004 A1, page 4, line 19 to        page 13, line 48,    -   European patent application EP 0 228 003 A1, page 3, line 24 to        page 5, line 40,    -   European patent application EP 0 634 431 A1, page 3, line 38 to        page 8, line 9, or    -   international patent application WO 92/15405, page 2, line 35 to        page 10, line 32, or    -   German patent application DE 44 37 535 A1.

The polyurethane resin is prepared using preferably the aliphatic,cycloaliphatic, aliphatic-cycloaliphatic, aromatic, aliphatic-aromaticand/or cycloaliphatic-aromatic polyisocyanates that are known to theskilled person.

As alcohol component for preparing the polyurethane resins, preferenceis given to using the saturated and unsaturated polyols of relativelyhigh molecular mass and of low molecular mass, and also, optionally,monoalcohols, in minor amounts, that are known to the skilled person.Low molecular mass polyols used are more particularly diols and, inminor amounts, triols, for introducing instances of branching. Examplesof suitable polyols of relatively high molecular mass are saturated orolefinically unsaturated polyester polyols and/or polyether polyols.Relatively high molecular mass polyols used are more particularlypolyester polyols, especially those having a number-average molecularweight of 400 to 5000 g/mol.

For hydrophilic stabilization and/or for increasing the dispersibilityin aqueous medium, the polyurethane resin preferably present may containparticular ionic groups and/or groups which can be converted into ionicgroups (potentially ionic groups). Polyurethane resins of this kind arereferred to in the context of the present invention as ionicallyhydrophilically stabilized polyurethane resins. Likewise present may benonionic hydrophilically modifying groups. Preferred, however, are theionically hydrophilically stabilized polyurethanes. In more preciseterms, the modifying groups are alternatively

-   -   functional groups which can be converted to cations by        neutralizing agents and/or quaternizing agents, and/or cationic        groups (cationic modification)        or    -   functional groups which can be converted to anions by        neutralizing agents, and/or anionic groups (anionic        modification)        and/or    -   nonionic hydrophilic groups (nonionic modification).

As the skilled person is aware, the functional groups for cationicmodification are, for example, primary, secondary and/or tertiary aminogroups, secondary sulfide groups and/or tertiary phosphine groups, moreparticularly tertiary amino groups and secondary sulfide groups(functional groups which can be converted to cationic groups byneutralizing agents and/or quaternizing agents). Mention should also bemade of the cationic groups—groups prepared from the aforementionedfunctional groups using neutralizing agents and/or quaternizing agentsknown to those skilled in the art—such as primary, secondary, tertiaryand/or quaternary ammonium groups, tertiary sulfonium groups and/orquaternary phosphonium groups, more particularly quaternary ammoniumgroups and tertiary sulfonium groups.

As is well known, the functional groups for anionic modification are,for example, carboxylic acid, sulfonic acid and/or phosphonic acidgroups, more particularly carboxylic acid groups (functional groupswhich can be converted to anionic groups by neutralizing agents), andalso anionic groups—groups prepared from the aforementioned functionalgroups using neutralizing agents known to the skilled person—such ascarboxylate, sulfonate and/or phosphonate groups.

The functional groups for nonionic hydrophilic modification arepreferably poly(oxyalkylene) groups, more particularly poly(oxyethylene)groups.

The ionically hydrophilic modifications can be introduced into thepolyurethane resin through monomers which contain the (potentially)ionic groups. The nonionic modifications are introduced, for example,through the incorporation of poly(ethylene) oxide polymers as lateral orterminal groups in the polyurethane molecules. The hydrophilicmodifications are introduced, for example, via compounds which containat least one group reactive toward isocyanate groups, preferably atleast one hydroxyl group. The ionic modification can be introduced usingmonomers which, as well as the modifying groups, contain at least onehydroxyl group. To introduce the nonionic modifications, preference isgiven to using the polyether diols and/or alkoxypoly(oxyalkylene)alcohols known to those skilled in the art.

As already indicated above, the polyurethane resin may preferably be agraft polymer by means of olefinically unsaturated monomers. In thiscase, then, the polyurethane is grafted, for example, with side groupsand/or side chains that are based on olefinically unsaturated monomers.These are more particularly side chains based on poly(meth)acrylates,with the systems in question then being thepolyurethane-poly(meth)acrylates already described above.Poly(meth)acrylates for the purposes of the present invention arepolymers or polymeric radicals which comprise monomers containingacrylate and/or methacrylate groups, and preferably consist of monomerscontaining acrylate groups and/or methacrylate groups. Side chains basedon poly(meth)acrylates are understood to be side chains which areconstructed during the graft polymerization, using monomers containing(meth)acrylate groups. In the graft polymerization, preference here isgiven to using more than 50 mol %, more particularly more than 75 mol %,especially 100 mol %, based on the total amount of the monomers used inthe graft polymerization, of monomers containing (meth)acrylate groups.

The side chains described are introduced into the polymer preferablyafter the preparation of a primary polyurethane resin dispersion (seealso description earlier on above). In this case the polyurethane resinpresent in the primary dispersion may contain lateral and/or terminalolefinically unsaturated groups via which, then, the graftpolymerization with the olefinically unsaturated compounds proceeds. Thepolyurethane resin for grafting may therefore be an unsaturatedpolyurethane resin. The graft polymerization is in that case a radicalpolymerization of olefinically unsaturated reactants. Also possible, forexample, is for the olefinically unsaturated compounds used for thegraft polymerization to contain at least one hydroxyl group. In thatcase it is also possible first for there to be attachment of theolefinically unsaturated compounds via these hydroxyl groups throughreaction with free isocyanate groups of the polyurethane resin. Thisattachment takes place instead of or in addition to the radical reactionof the olefinically unsaturated compounds with the lateral and/orterminal olefinically unsaturated groups optionally present in thepolyurethane resin. This is then followed again by the graftpolymerization via radical polymerization, as described earlier onabove. The result in any case is polyurethane resins grafted witholefinically unsaturated compounds, preferably olefinically unsaturatedmonomers.

As olefinically unsaturated compounds with which the polyurethane resinis preferably grafted it is possible to use virtually all radicallypolymerizable, olefinically unsaturated, and organic monomers which areavailable to the skilled person for these purposes. A number ofpreferred monomer classes may be specified by way of example:

-   -   hydroxyalkyl esters of (meth)acrylic acid or of other alpha-,        beta-ethylenically unsaturated carboxylic acids,    -   (meth)acrylic acid alkyl and/or cycloalkyl esters having up to        20 carbon atoms in the alkyl radical,    -   ethylenically unsaturated monomers comprising at least one acid        group, more particularly exactly one carboxyl group, such as        (meth)acrylic acid, for example,    -   vinyl esters of monocarboxylic acids which are branched in        alpha-position and have 5 to 18 carbon atoms,    -   reaction products of (meth)acrylic acid with the glycidyl ester        of a monocarboxylic acid which is branched in alpha-position and        has 5 to 18 carbon atoms,    -   further ethylenically unsaturated monomers such as olefins        (ethylene for example), (meth)acrylamides, vinylaromatic        hydrocarbons (styrene for example), vinyl compounds such as        vinyl chloride and/or vinyl ethers such as ethyl vinyl ether.

Used with preference are monomers containing (meth)acrylate groups, andso the side chains attached by grafting are poly(meth)acrylate-basedside chains.

The lateral and/or terminal olefinically unsaturated groups in thepolyurethane resin, via which the graft polymerization with theolefinically unsaturated compounds can proceed, are introduced into thepolyurethane resin preferably via particular monomers. These particularmonomers, in addition to an olefinically unsaturated group, alsoinclude, for example, at least one group that is reactive towardisocyanate groups. Preferred are hydroxyl groups and also primary andsecondary amino groups. Especially preferred are hydroxyl groups.

The monomers described through which the lateral and/or terminalolefinically unsaturated groups may be introduced into the polyurethaneresin may also, of course, be employed without the polyurethane resinbeing additionally grafted thereafter with olefinically unsaturatedcompounds. It is preferred, however, for the polyurethane resin to begrafted with olefinically unsaturated compounds.

The polyurethane resin preferably present may be a self-crosslinkingand/or externally crosslinking binder. The polyurethane resin preferablycomprises reactive functional groups through which external crosslinkingis possible. In that case there is preferably at least one crosslinkingagent in the pigmented aqueous basecoat material. The reactivefunctional groups through which external crosslinking is possible aremore particularly hydroxyl groups. With particular advantage it ispossible, for the purposes of the method of the invention, to usepolyhydroxy-functional polyurethane resins. This means that thepolyurethane resin contains on average more than one hydroxyl group permolecule.

The polyurethane resin is prepared by the customary methods of polymerchemistry. This means, for example, the polymerization ofpolyisocyanates and polyols to polyurethanes, and the graftpolymerization that preferably then follows with olefinicallyunsaturated compounds. These methods are known to the skilled person andcan be adapted individually. Exemplary preparation processes andreaction conditions can be found in European patent EP 0521 928 B1, page2, line 57 to page 8, line 16.

The polyurethane resin preferably present possesses, for example, ahydroxyl number of 0 to 250 mg KOH/g, but more particularly from 20 to150 mg KOH/g. The acid number of the polyurethane resin is preferably 5to 200 mg KOH/g, more particularly 10 to 40 mg KOH/g. The hydroxylnumber is determined in the context of the present invention inaccordance with DIN 53240.

The polyurethane resin content is preferably between 5 and 80 wt %, morepreferably between 8 and 70 wt %, and more preferably between 10 and 60wt %, based in each case on the film-forming solids of the basecoatmaterial.

Irrespective of occasional reference in the context of the presentinvention both to polyurethanes (also called polyurethane resins) and topolyurethane-poly(meth)acrylates, the expression “polyurethanes”, as ageneric term, embraces the polyurethane-poly(meth)acrylates. If,therefore, no distinction is made between the two classes of polymer ina particular passage, but instead only the expression “polyurethane” or“polyurethane resin” is stated, both polymer classes are encompassed.

By film-forming solids, corresponding ultimately to the binder fraction,is meant the nonvolatile weight fraction of the basecoat material,without pigments and, where appropriate, fillers. The film-formingsolids can be determined as follows: A sample of the pigmented aqueousbasecoat material (approximately 1 g) is admixed with 50 to 100 timesthe amount of tetrahydrofuran and then stirred for around 10 minutes.The insoluble pigments and any fillers are then removed by filtrationand the residue is rinsed with a little THF, the THF being removed fromthe resulting filtrate on a rotary evaporator. The residue of thefiltrate is dried at 120° C. for two hours and the resultingfilm-forming solids are obtained by weighing.

The sum total of the weight-percentage fractions, based on the totalweight of the pigmented aqueous basecoat material, of all polyurethaneresins is preferably 2 to 40 wt %, more preferably 2.5 to 30 wt %, andvery preferably 3 to 25 wt %.

There is preferably also a thickener present. Suitable thickeners areinorganic thickeners from the group of the phyllosilicates. As well asthe inorganic thickeners, however, it is also possible to use one ormore organic thickeners. These are preferably selected from the groupconsisting of (meth)acrylic acid-(meth)acrylate copolymer thickeners, asfor example the commercial product Rheovis AS 1130 (BASF), and ofpolyurethane thickeners, as for example the commercial product RheovisPU 1250 (BASF). The thickeners used are different from the binders used.

Furthermore, the pigmented aqueous basecoat material may furthercomprise at least one adjuvant. Examples of such adjuvants are saltswhich can be decomposed thermally without residue or substantiallywithout residue, resins as binders that are curable physically,thermally and/or with actinic radiation and are different from theabove-described polymers, further crosslinking agents, organic solvents,reactive diluents, transparent pigments, fillers, molecularly disperselysoluble dyes, nanoparticles, light stabilizers, antioxidants, deaeratingagents, emulsifiers, slip additives, polymerization inhibitors,initiators of radical polymerizations, adhesion promoters, flow controlagents, film-forming assistants, sag control agents (SCAs), flameretardants, corrosion inhibitors, waxes, siccatives, biocides, andmatting agents. Also included may be thickeners such as organicthickeners from the group of the phyllosilicates or organic thickenerssuch as (meth)acrylic acid-(meth)acrylate copolymer thickeners, or elsepolyurethane thickeners, which are different from the binders used.

Suitable adjuvants of the aforementioned kind are known, for example,from

-   -   German patent application DE 199 48 004 A1, page 14, line 4, to        page 17, line 5,    -   German patent DE 100 43 405 C1 column 5, paragraphs [0031] to        [0033].

They are used in the customary and known amounts.

The solids content of the basecoat materials of the invention may varyaccording to the requirements of the case in hand. The solids content isguided primarily by the viscosity required for application, moreparticularly for spray application, and so may be adjusted by theskilled person on the basis of his or her general art knowledge,optionally with assistance from a few exploratory tests.

The solids content of the basecoat materials is preferably 5 to 70 wt %,more preferably 8 to 60 wt %, and very preferably 12 to 55 wt.

By solids content (nonvolatile fraction) is meant that weight fractionwhich remains as a residue on evaporation under specified conditions. Inthe present application, the solids content, unless explicitly indicatedotherwise, is determined in accordance with DIN EN ISO 3251. This isdone by evaporating the basecoat material (test sample 1.0 g) at 130° C.for 60 minutes.

Unless indicated otherwise, this test method is likewise employed inorder to determine, for example, the fraction of various components ofthe basecoat material as a proportion of the total weight of thebasecoat material. Thus, for example, the solids content of a dispersionof a polyurethane resin which is to be added to the basecoat materialmay be determined correspondingly in order to ascertain the fraction ofthis polyurethane resin as a proportion of the overall composition. Themethod is likewise employed in order to determine the amount or aproperty of various further components. If, for example, the amount or aproperty of a component (a) present in the solvent, able to be used forpreparing reaction products of the invention, is determined, this methodis employed. In this connection, reference may be made, for example, tothe isocyanate content of a component (a) (that is, the component (a)per se (solid body) and without solvent). The situation is the same, forexample, with the OH number of a polymer to be used in the basecoatmaterial.

The basecoat material of the invention is aqueous. The expression“aqueous” is known in this context to the skilled person. The phraserefers in principle to a basecoat material which is not basedexclusively on organic solvents, i.e., does not contain exclusivelyorganic-based solvents as its solvents but instead, in contrast,includes a significant fraction of water as solvent. “Aqueous” for thepurposes of the present invention should preferably be understood tomean that the coating composition in question, more particularly thebasecoat material, has a water fraction of at least 40 wt %, preferablyat least 50 wt %, very preferably at least 60 wt %, based in each caseon the total amount of the solvents present (i.e., water and organicsolvents). Preferably in turn, the water fraction is 40 to 90 wt %, moreparticularly 50 to 80 wt %, very preferably 60 to 75 wt %, based in eachcase on the total amount of the solvents present.

The basecoat materials employed in accordance with the invention may beproduced using the mixing assemblies and mixing techniques that arecustomary and known for producing basecoat materials.

The Method of the Invention and the Multicoat Paint System of theInvention

A further aspect of the present invention is a method for producing amulticoat paint system, by

(1) applying a pigmented aqueous basecoat material to a substrate,(2) forming a polymer film from the coating material applied in stage(1),(3) applying a clearcoat material to the resultant basecoat, and then(4) curing the basecoat together with the clearcoat,which comprises using in stage (1) a pigmented aqueous basecoat materialwhich comprises at least one reaction product of the invention. All ofthe above observations relating to the reaction product of the inventionand to the pigmented aqueous basecoat material are also valid in respectof the method of the invention. This is true more particularly also ofall preferred, very preferred, and especially preferred features.

Said method is preferably used to produce multicoat color paint systems,effect paint systems, and color and effect paint systems.

The pigmented aqueous basecoat material used in accordance with theinvention is commonly applied to metallic or plastics substrates thathave been pretreated with surfacer or primer-surfacer. Said basecoatmaterial may optionally also be applied directly to the plasticssubstrate.

Where a metallic substrate is to be coated, it is preferably furthercoated with an electrocoat system before the surfacer or primer-surfaceris applied.

Where a plastics substrate is being coated, it is preferably alsopretreated before the surfacer or primer-surfacer is applied. Thetechniques most frequently employed for such pretreatment are those offlaming, plasma treatment, and corona discharge. Flaming is used withpreference.

Application of the pigmented aqueous basecoat material of the inventionto metallic substrates already coated, as described above, with curedelectrocoat systems and/or surfacers may take place in the filmthicknesses customary within the automobile industry, in the range, forexample, of 5 to 100 micrometers, preferably 5 to 60 micrometers (dryfilm thickness). This is done using spray application methods, as forexample compressed air spraying, airless spraying, high-speed rotation,electrostatic spray application (ESTA), alone or in conjunction with hotspray application, such as for example, hot air spraying.

Following the application of the pigmented aqueous basecoat material, itcan be dried by known methods. For example, (1-component) basecoatmaterials, which are preferred, can be flashed at room temperature for 1to 60 minutes and subsequently dried, preferably at optionally slightlyelevated temperatures of 30 to 90° C. Flashing and drying in the contextof the present invention mean the evaporation of organic solvents and/orwater, as a result of which the paint becomes drier but has not yetcured or not yet formed a fully crosslinked coating film.

Then a commercial clearcoat material is applied, by likewise commonmethods, the film thicknesses again being within the customary ranges,for example 5 to 100 micrometers (dry film thickness).

After the clearcoat material has been applied, it can be flashed at roomtemperature for 1 to 60 minutes, for example, and optionally dried. Theclearcoat material is then cured together with the applied pigmentedbasecoat material. In the course of these procedures, crosslinkingreactions occur, for example, to produce on a substrate a multicoatcolor and/or effect paint system of the invention. Curing takes placepreferably thermally at temperatures from 60 to 200° C. Thermally curingbasecoat materials are preferably those which comprise as additionalbinder a polyurethane resin and as crosslinking agent an aminoplastresin or a blocked or nonblocked polyisocyanate, preferably anaminoplast resin. Among the aminoplast resins, melamine resins arepreferred.

In one particular embodiment, the method for producing a multicoat paintsystem comprises the following steps:

producing a cured electrocoat film on the metallic substrate byelectrophoretic application of an electrocoat material to the substrateand subsequent curing of the electrocoat material,producing (i) a basecoat film or (ii) a plurality of basecoat filmsdirectly following one another directly on the cured electrocoat film by(i) application of an aqueous basecoat material directly to theelectrocoat film, or (ii) directly successive application of two or morebasecoat materials to the electrocoat film,producing a clearcoat film directly on (i) the basecoat film or (ii) theuppermost basecoat film, by application of a clearcoat material directlyto (i) one basecoat film or (ii) the uppermost basecoat film,where (i) one basecoat material or (ii) at least one of the basecoatmaterials is a basecoat material of the invention,joint curing of the basecoat film (i) or of the basecoat films (ii) andalso of the clearcoat film.

In the latter embodiment, then, in comparison to the above-describedstandard methods, there is no application and separate curing of acommonplace surfacer. Instead, all of the films applied to theelectrocoat film are cured jointly, thereby making the overall operationmuch more economical. Nevertheless, in this way, and particularlythrough the use of a basecoat material of the invention comprising areaction product of the invention, multicoat paint systems areconstructed which have outstanding mechanical stability and adhesion andhence are particularly technologically outstanding.

The application of a coating material directly to a substrate ordirectly to a previously produced coating film is understood as follows:The respective coating material is applied in such a way that thecoating film produced from it is disposed on the substrate (on the othercoating film) and is in direct contact with the substrate (with theother coating film). Between coating film and substrate (other coatingfilm), therefore, there is more particularly no other coat. Without thedetail “direct”, the applied coating film, while disposed on thesubstrate (the other film), need not necessarily be present in directcontact. More particularly, further coats may be disposed between them.In the context of the present invention, therefore, the following is thecase: In the absence of particularization as to “direct”, there isevidently no restriction to “direct”.

Plastics substrates are coated basically in the same way as metallicsubstrates. Here, however, in general, curing takes place atsignificantly lower temperatures, of 30 to 90° C. Preference istherefore given to the use of two-component clearcoat materials.

The method of the invention can be used to paint metallic andnonmetallic substrates, more particularly plastics substrates,preferably automobile bodies or components thereof.

The method of the invention can be used further for dual finishing inOEM finishing. This means that a substrate which has been coated bymeans of the method of the invention is painted for a second time,likewise by means of the method of the invention.

The invention relates further to multicoat paint systems which areproducible by the method described above. These multicoat paint systemsare to be referred to below as multicoat paint systems of the invention.

All of the above observations relating to the reaction product of theinvention and to the pigmented aqueous basecoat material are also validin respect of said multicoat paint system and of the method of theinvention. This is also true especially of all the preferred, morepreferred and most preferred features.

The multicoat paint systems of the invention are preferably multicoatcolor paint systems, effect paint systems, and color and effect paintsystems.

A further aspect of the invention relates to the method of theinvention, wherein said substrate from stage (1) is a multicoat paintsystem having defects. This substrate/multicoat paint system, whichpossesses defects, is therefore an original finish, which is to berepaired or completely recoated.

The method of the invention is suitable accordingly for repairingdefects on multicoat paint systems. Film defects are generally faults onand in the coating, usually named according to their shape or theirappearance. The skilled person is aware of a host of possible kinds ofsuch film defects. They are described for example in Römpp-Lexikon Lackeund Druckfarben, Georg Thieme Verlag, Stuttgart, New York, 1998, page235, “Film defects”.

The multicoat paint systems produced by means of the method of theinvention may likewise have such defects. In one preferred embodiment ofthe method of the invention, therefore, the substrate from stage (1) isa multicoat paint system of the invention which exhibits defects.

These multicoat paint systems are produced preferably on automobilebodies or parts thereof, by means of the method of the invention,identified above, in the context of automotive OEM finishing. Where suchdefects occur directly after OEM finishing has taken place, they arerepaired immediately. The term “OEM automotive refinishing” is thereforealso used. Where only small defects require repair, only the “spot” isrepaired, and the entire body is not completely recoated (dual coating).The former process is called “spot repair”. The use of the method of theinvention for remedying defects on multicoat paint systems (originalfinishes) of the invention in OEM automotive refinishing, therefore, isparticularly preferred.

Where reference is made, in the context of the present invention, to theautomotive refinish segment, in other words when the repair of defectsis the topic, and the substrate specified is a multicoat paint systempossessing defects, this of course means that this substrate/multicoatpaint system with defects (original finish) is generally located on aplastic substrate or on a metallic substrate as described above.

So that the repaired site has no color difference from the rest of theoriginal finish, it is preferred for the aqueous basecoat material usedin stage (1) of the method of the invention for repairing defects to bethe same as that which was used to produce the substrate/multicoat paintsystem with defects (original finish).

The observations above concerning the reaction product of the inventionand the aqueous pigmented basecoat material therefore are also valid forthe use, under discussion, of the method of the invention for repairingdefects on a multicoat paint system. This is also true in particular ofall stated preferred, very preferred, and especially preferred features.It is additionally preferred for the multicoat paint systems of theinvention that are to be repaired to be multicoat color paint systems,effect paint systems, and color and effect paint systems.

The above-described defects on the multicoat paint system of theinvention can be repaired by means of the above-described method of theinvention. For this purpose, the surface to be repaired on the multicoatpaint system may initially be abraded. The abrading is preferablyperformed by partially sanding, or sanding off, only the basecoat andthe clearcoat, optionally only the clearcoat, from the original finish,but not sanding off the primer layer and surfacer layer that aregenerally situated beneath them. In this way, during the refinish, thereis no need in particular for renewed application of specialty primersand primer-surfacers. This form of abrading has become establishedespecially in the OEM automotive refinishing segment, since here, incontrast to refinishing in a workshop, generally speaking, defects occuronly in the basecoat and/or clearcoat region, but do not, in particular,occur in the region of the underlying surfacer and primer coats. Defectsin the latter coats are more likely to be encountered in the workshoprefinish sector. Examples include paint damage such as scratches, whichare produced, for example, by mechanical effects and which often extenddown to the substrate surface (metallic or plastic substrate).

After the abrading procedure, the pigmented aqueous basecoat material isapplied to the defect site in the original finish by spray application:for example, by pneumatic atomization. After the pigmented aqueousbasecoat material has been applied, it can be dried by known methods.For example, the basecoat material may be dried at room temperature for1 to 60 minutes and subsequently dried at optionally slightly elevatedtemperatures of 30 to 80° C. Flashing and drying for the purposes of thepresent invention means evaporation of organic solvents and/or water,whereby the coating material is as yet not fully cured. For the purposesof the present invention it is preferred for the basecoat material tocomprise a polyurethane resin as binder and an aminoplast resin,preferably a melamine resin, as crosslinking agent.

A commercial clearcoat material is subsequently applied, by techniquesthat are likewise commonplace. Following application of the clearcoatmaterial, it may be flashed off at room temperature for 1 to 60 minutes,for example, and optionally dried. The clearcoat material is then curedtogether with the applied pigmented basecoat material.

In the case of so-called low-temperature baking, curing takes placepreferably at temperatures of 20 to 90° C. Preference here is given tousing two-component clearcoat materials. If, as described above, apolyurethane resin is used as further binder and an aminoplast resin isused as crosslinking agent, there is only slight crosslinking by theaminoplast resin in the basecoat film at these temperatures. Here, inaddition to its function as a curing agent, the aminoplast resin alsoserves for plasticizing and may assist pigment wetting. Besides theaminoplast resins, nonblocked isocyanates may also be used. Depending onthe nature of the isocyanate used, they crosslink at temperatures fromas low as 20° C. Waterborne basecoat materials of this kind are then ofcourse generally formulated as two-component systems.

In the case of what is called high-temperature baking, curing isaccomplished preferably at temperatures of 130 to 160° C. Here bothone-component and two-component clearcoat materials are used. If, asdescribed above, a polyurethane resin is used as further binder and anaminoplast resin is used as crosslinking agent, there is crosslinking bythe aminoplast resin in the basecoat film at these temperatures.

A further aspect of the present invention is the use of the reactionproduct of the invention in pigmented aqueous basecoat materials forimproving the adhesion and the stonechip resistance of paint systemsproduced using the basecoat material.

The invention is illustrated below using examples.

EXAMPLES Determination of the Number-Average Molecular Weight:

The number-average molecular weight was determined by means of vaporpressure osmosis. Measurement took place using a vapor pressureosmometer (model 10.00 from Knauer) on concentration series of the testcomponent in toluene at 50° C. with benzophenone as calibration compoundfor the determination of the experimental calibration constant of theinstrument used (according to E. Schröder, G. Müller, K.-F. Arndt,“Leitfaden der Polymercharakterisierung” [Principles of polymercharacterization], Academy-Verlag, Berlin, pp. 47-54, 1982, where thecalibration compound used was in fact benzil).

Isocyanate Content:

The isocyanate content, also referred to hereinafter as NCO content, isdetermined by adding an excess of a 2% strength N,N-dibutylaminesolution in xylene to a homogeneous solution of the samples inacetone/N-ethyl-pyrrolidone (1:1 vol %), by potentiometricback-titration of the amine excess with 0.1 N hydrochloric acid inaccordance with DIN EN ISO 3251, DIN EN ISO 11909 and DIN EN ISO 14896.Via the fraction of a component (solid body) in solution it is possibleto calculate back to the NCO content of the component per se. The NCOcontent therefore indicates the weight-based percentage fraction of NCOgroups as a proportion of the total weight of the respective component.

Production of Inventive Reaction Products (IR) and Also of ReactionProducts Used for Comparison (CR): IR1:

In a 4 l stainless steel reactor equipped with anchor stirrer,thermometer, condenser, 466.8 g of isophorone diisocyanate, 918 g ofmethyl ethyl ketone, 910 g of PolyTHF650 (from BASF SE) with an OHnumber of 172 mg KOH/g (1.4 mol), and 0.69 g of dibutyltin dilaurate areheated to 80° C. This temperature is maintained until the NCO content,based on the solids content of the solution, is constant and is in arange from 2.0 to 2.1% (thus corresponding to the NCO content ofcomponent (a)). At this point 150 g of trimethylolpropane are added andthe temperature stated above is further maintained until the NCO valuehas reached less than 0.1%. Thereafter the methyl ethyl ketone isremoved by distillation under reduced pressure down to a level of lessthan 0.5%, and the resulting resin is diluted at 80° C. with 640 g ofbutyl glycol.

The solids content of the resin solution is 67% (measured at 130° C. for1 h in a forced air oven on a 1 g sample with addition of 1 ml of methylethyl ketone)

Number-average molecular weight (vapor pressure osmosis): 2400 g/mol

Viscosity 50% in butyl glycol: 2940 mPas (measured at 23° C. using aBrookfield CAP 2000+ rotary viscometer, spindle 3, shear rate: 750 s⁻¹).

IR2:

In a 4 l stainless steel reactor equipped with anchor stirrer,thermometer, condenser, 382.3 g of isophorone diisocyanate, 1401 g ofmethyl ethyl ketone, 1720 g of PolyTHF2000 (from BASF SE) with an OHnumber of 56 mg KOH/g (0.86 mol), and 1.05 g of dibutyltin dilaurate areheated to 80° C. This temperature is maintained until the NCO content,based on the solids content of the solution, is constant and is in arange from 1.6% to 1.7% (thus corresponding to the NCO content ofcomponent (a)). At this point 179 g of trimethylolpropane are added andthe temperature stated above is further maintained until the NCO valuehas reached less than 0.1%. Thereafter the methyl ethyl ketone isremoved by distillation under reduced pressure down to a level of lessthan 0.5%, and the resulting resin is diluted at 80° C. with 570 g ofbutyl glycol.

The solids content of the resin solution is 78% (measured at 130° C. for1 h in a forced air oven on a 1 g sample with addition of 1 ml of methylethyl ketone)

Number-average molecular weight (vapor pressure osmosis): 2600 g/mol

Viscosity 50% in butyl glycol: 3475 mPas (measured at 23° C. using aBrookfield CAP 2000+ rotary viscometer, spindle 3, shear rate: 750 s⁻¹).

CR1:

The reaction product used for comparison was a polyester preparedaccording to example D, column 16, lines 37 to 59 of DE 4009858 A, theorganic solvent used being butyl glycol rather than butanol, meaningthat solvents present are butyl glycol and water. The correspondingdispersion of the polyester has a solids content of 60 wt %.

Preparation of Aqueous Basecoat Materials

The following should be taken into account regarding formulationconstituents and amounts thereof as indicated in the tables hereinafter.When reference is made to a commercial product or to a preparationprotocol described elsewhere, the reference, independently of theprincipal designation selected for the constituent in question, is toprecisely this commercial product or precisely the product prepared withthe referenced protocol.

Accordingly, where a formulation constituent possesses the principaldesignation “melamine-formaldehyde resin” and where a commercial productis indicated for this constituent, the melamine-formaldehyde resin isused in the form of precisely this commercial product. Any furtherconstituents present in the commercial product, such as solvents, musttherefore be taken into account if conclusions are to be drawn about theamount of the active substance (of the melamine-formaldehyde resin).

If, therefore, reference is made to a preparation protocol for aformulation constituent, and if such preparation results, for example,in a polymer dispersion having a defined solids content, then preciselythis dispersion is used. The overriding factor is not whether theprincipal designation that has been selected is the term “polymerdispersion” or merely the active substance, as for example “polymer”,“polyester” or “polyurethane-modified polyacrylate”. This must be takeninto account if conclusions are to be drawn concerning the amount of theactive substance (of the polymer).

All proportions indicated in the tables are parts by weight.

Preparation of a Non-Inventive Waterborne Basecoat Material 1

The components listed under “Aqueous phase” in table A were stirredtogether in the order stated to form an aqueous mixture. In the nextstep, an organic mixture was prepared from the components listed under“Organic phase”. The organic mixture was added to the aqueous mixture.The combined mixtures were then stirred for 10 minutes and adjustedusing deionized water and dimethylethanolamine to a pH of 8 and to aspray viscosity of 58 mPas under a shearing load of 1000 s⁻¹, measuredusing a rotational viscometer (Rheomat RM 180 instrument fromMettler-Toledo) at 23° C.

TABLE A Waterborne basecoat material 1 Component Parts by weight Aqueousphase Aqueous solution of 3% sodium 27 lithium magnesium phyllosilicateLaponite ® RD (from Altana-Byk) and 3% Pluriol ® P900 (from BASF SE)Deionized water 15.9 Butyl glycol (from BASF SE) 3.5 Hydroxy-functional,polyurethane- 2.4 modified polyacrylate; prepared as per page 7, line 55to page 8, line 23 of DE 4437535 A1 50 wt % strength solution of 0.2Rheovis ® PU 1250 (BASF SE) in butyl glycol, rheological agent CR1 2.5TMDD 50% BG (from BASF SE), 52% 1.2 strength solution of 2,4,7,9-tetramethyl-5-decyne-4,7-diol in butyl glycol Luwipal ® 052 (from BASFSE), 4.7 melamine-formaldehyde resin 10% strength solution of N,N- 0.5dimethylethanolamine (from BASF SE) in water Polyurethane-based graftcopolymer; 19.6 prepared in analogy to DE 19948004 A1 (page 27 - example2) Isopropanol (from BASF SE) 1.4 Byk-347 ® (from Altana-Byk) 0.5Pluriol ® P900 (from BASF SE) 0.3 Tinuvin ® 384-2 (from BASF SE) 0.6Tinuvin ® 123 (from BASF SE) 0.3 Carbon black paste 4.3 Blue paste 11.4Mica slurry 2.8 Organic phase Aluminum pigment (from Altana- 0.3 Eckart)Butyl glycol (from BASF SE) 0.3 Polyurethane-based graft copolymer; 0.3prepared in analogy to DE 19948004 A1 (page 27 - example 2)

Preparation of Blue Paste:

The blue paste was prepared from 69.8 parts by weight of an acrylatedpolyurethane dispersion prepared as per international patent applicationWO 91/15528, binder dispersion A, 12.5 parts by weight of Paliogen® BlueL 6482, 1.5 parts by weight of dimethylethanolamine (10% strength in DIwater), 1.2 parts by weight of a commercial polyether (Pluriol® P900from BASF SE), and 15 parts by weight of deionized water.

Preparation of Carbon Black Paste:

The carbon black paste was prepared from 25 parts by weight of anacrylated polyurethane dispersion prepared as per international patentapplication WO 91/15528, binder dispersion A, 10 parts by weight ofcarbon black, 0.1 part by weight of methyl isobutyl ketone, 1.45 partsby weight of dimethylethanolamine (10% strength in DI water), 2 parts byweight of a commercial polyether (Pluriol® P900 from BASF SE), and 61.45parts by weight of deionized water.

Preparation of the Mica Slurry:

The mica slurry was obtained by using a stirring element to mix 1.5parts by weight of polyurethane-based graft copolymer, prepared in ananalogy to DE 19948004 A1 (page 27—example 2), and 1.3 parts by weightof the commercial Mica Mearlin Ext. Fine Violet 539V from Merck.

Preparation of Inventive Waterborne Basecoat Materials I1 and I2

The waterborne basecoat materials I1 and I2 were prepared in analogy totable A, but using the reaction product IR1 (waterborne basecoatmaterial I1) or the reaction product IR2 (waterborne basecoat materialI2) in place of CR1. The proportion used of the reaction product IR1 orIR2 was respectively the same, through compensation of the amount ofsolvent and/or consideration of the solids content of the component tobe added.

TABLE B Basecoat materials 1, I1 and I2 Reaction product Waterbornebasecoat material 1 CR1 Waterborne basecoat material I1 IR1 Waterbornebasecoat material I2 IR2

Comparison Between Waterborne Basecoat Materials 1 and I1, I2 StonechipResistance:

For the determination of the stonechip resistance, the multicoat paintsystems were produced according to the following general protocol:

The substrate used was a steel panel with dimensions of 10×20 cm, coatedwith a cathodic e-coat (cathodic electrocoat).

Applied to this panel first of all was the respective basecoat material(table B), applied pneumatically with a target film thickness (dry filmthickness) of 20 micrometers. After the basecoat had been flashed atroom temperature for 1 minute, it was subjected to interim drying in aforced air oven at 70° C. for 10 minutes. Over the interim-driedwaterborne basecoat, a customary two-component clearcoat material wasapplied with a target film thickness (dry film thickness) of 40micrometers. The resulting clearcoat was flashed at room temperature for20 minutes. The waterborne basecoat and the clearcoat were subsequentlycured in a forced air oven at 160° C. for 30 minutes.

The resulting multicoat paint systems were tested for their stonechipresistance. This was done using the stonechip test of DIN 55966-1. Theresults of the stonechip test were assessed in accordance with DIN ENISO 20567-1. Lower values represent better stonechip resistance.

The results are found in table 1. The waterborne basecoat material (WBM)detail indicates which WBM was used in the particular multicoat paintsystem.

TABLE 1 Stonechip resistance of waterborne basecoat materials 1 and I1,I2 WBM Stonechip outcome   1 2.5 I1 1.5 I2 1.5

The results emphasize that the use of the inventive reaction products inbasecoat materials significantly increases the stonechip resistance bycomparison with the waterborne basecoat material 1.

Preparation of a Non-Inventive Waterborne Basecoat Material 2

The components listed under “Aqueous phase” in table C were stirredtogether in the order stated to form an aqueous mixture. The mixture wasthen stirred for 10 minutes and adjusted using deionized water anddimethylethanolamine to a pH of 8 and to a spray viscosity of 58 mPasunder a shearing load of 1000 s⁻¹, measured using a rotationalviscometer (Rheomat RM 180 instrument from Mettler-Toledo) at 23° C.

TABLE C Waterborne basecoat material 2 Component Parts by weight Aqueousphase Aqueous solution of 3% sodium 14 lithium magnesium phyllosilicateLaponite ® RD (from Altana-Byk) and 3% Pluriol ® P900 (from BASF SE)Deionized water 16 Butyl glycol (from BASF SE) 1.4 CR1 2.3 10 wt %strength solution of 6 Rheovis ® AS 1130 (BASF SE) in deionized water,rheological agent TMDD 50% BG (from BASF SE), 52% 1.6 strength solutionof 2,4,7,9- tetramethyl-5-decyne-4,7-diol in butyl glycol Cymel ® 1133(from Cytec), melamine- 5.9 formaldehyde resin 10% strength solution ofN,N-dimethyl- 0.4 ethanolamine (from BASF SE) in water Polyurethanedispersion - prepared 20 as per WO 92/15405 (page 14, line 13 to page15, line 28) 2-Ethylhexanol (from BASF SE) 3.5 Triisobutyl phosphate(from Bayer) 2.5 Nacure ® 2500 (from King Industries) 0.6 White paste 24Carbon black paste 1.8

Preparation of Carbon Black Paste:

The carbon black paste was prepared from 25 parts by weight of anacrylated polyurethane dispersion prepared as per international patentapplication WO 91/15528, binder dispersion A, 10 parts by weight ofcarbon black, 0.1 part by weight of methyl isobutyl ketone, 1.45 partsby weight of dimethylethanolamine (10% strength in DI water), 2 parts byweight of a commercial polyether (Pluriol® P900 from BASF SE), and 61.45parts by weight of deionized water.

Preparation of White Paste:

The white paste was prepared from 43 parts by weight of an acrylatedpolyurethane dispersion prepared as per international patent applicationWO 91/15528, binder dispersion A, 50 parts by weight of titanium rutile2310, 3 parts by weight of 1-propoxy-2-propanol, and 4 parts by weightof deionized water.

Preparation of Inventive Waterborne Basecoat Materials I3 and I4

The waterborne basecoat materials I3 and I4 were prepared in analogy totable C, but using the reaction product IR1 (waterborne basecoatmaterial 13) or the reaction product IR2 (waterborne basecoat material14) in place of CR1. The proportion used of the reaction product IR1 orIR2 was respectively the same, through compensation of the amount ofsolvent and/or consideration of the solids content of the component tobe added.

TABLE D Basecoat materials 2, I3 and I4 Reaction product Waterbornebasecoat material 2 CR1 Waterborne basecoat material I3 IR1 Waterbornebasecoat material I4 IR2

Preparation of a Non-Inventive Waterborne Basecoat Material 3

The components listed under “Aqueous phase” in table E were stirredtogether in the order stated to form an aqueous mixture. In the nextstep, an organic mixture was prepared from the components listed under“Organic phase”. The organic mixture was added to the aqueous mixture.The combined mixtures were then stirred for 10 minutes and adjustedusing deionized water and dimethylethanolamine to a pH of 8 and to aspray viscosity of 58 mPas under a shearing load of 1000 s⁻¹, measuredusing a rotational viscometer (Rheomat RM 180 instrument fromMettler-Toledo) at 23° C.

TABLE E Waterborne basecoat material 3 Component Parts by weight Aqueousphase Aqueous solution of 3% sodium 20.35 lithium magnesiumphyllosilicate Laponite ® RD (from Altana-Byk) and 3% Pluriol ® P900(from BASF SE) Deionized water 17.27 Butyl glycol (from BASF SE) 2.439Hydroxy-functional, polyurethane- 2.829 modified polyacrylate; preparedas per page 7, line 55 to page 8, line 23 of DE 4437535 A1 50 wt %strength solution of 0.234 Rheovis ® PU 1250 (BASF SE) in butyl glycol,rheological agent 10 wt % strength solution of 4.976 Rheovis ® AS 1130(BASF SE) in deionized water, rheological agent TMDD 50% BG (from BASFSE), 52% 1.317 strength solution of 2,4,7,9-tetramethyl-5-decyne-4,7-diol in butyl glycol Cymel ® 1133 (from Cytec),melamine- 3.512 formaldehyde resin 10% strength solution ofN,N-dimethyl- 1.356 ethanolamine (from BASF SE) in water Polyurethanedispersion - prepared 24.976 as per WO 92/15405 (page 14, line 13 topage 15, line 28) Isopropanol (from BASF SE) 1.659 Byk-347 ® (fromAltana-Byk) 0.537 Pluriol ® P900 (from BASF SE) 0.39 2-Ethylhexanol(from BASF SE) 1.854 Triisobutyl phosphate (from Bayer) 1.151 Nacure ®2500 (from King Industries) 0.39 Tinuvin ® 384-2 (from BASF SE) 0.605Tinuvin ® 123 (from BASF SE) 0.39 Blue paste 0.605 Organic phaseAluminum pigment 1 (from Altana- 4.585 Eckart) Aluminum pigment 2 (fromAltana- 0.907 Eckart) Butyl glycol (from BASF SE) 3.834Polyurethane-based graft copolymer; 3.834 prepared in analogy to DE19948004 A1 (page 27 - example 2)

Preparation of Blue Paste:

The blue paste was prepared from 69.8 parts by weight of an acrylatedpolyurethane dispersion prepared as per international patent applicationWO 91/15528, binder dispersion A, 12.5 parts by weight of Paliogen® BlueL 6482, 1.5 parts by weight of dimethylethanolamine (10% strength in DIwater), 1.2 parts by weight of a commercial polyether (Pluriol® P900from BASF SE), and 15 parts by weight of deionized water.

Comparison of Waterborne Basecoat Materials 2 and I3, I4

For the determination of the stonechip resistance, the multicoat paintsystems were produced according to the following general protocol:

The substrate used was a steel panel with dimensions of 10×20 cm, coatedwith a cathodic e-coat.

Applied to this panel first of all was the respective basecoat material(table D), which was applied with a target film thickness (dry filmthickness) of 20 micrometers. After the basecoat had been flashed atroom temperature for 4 minutes, the waterborne basecoat material 3 wasapplied in a target film thickness (dry film thickness) of 20micrometers, followed by flashing at room temperature for 4 minutes andthen by interim drying in a forced air oven at 70° C. for 10 minutes.Over the interim-dried waterborne basecoat, a customary two-componentclearcoat material was applied with a target film thickness (dry filmthickness) of 40 micrometers. The resulting clearcoat was flashed atroom temperature for 20 minutes. The waterborne basecoat and theclearcoat were subsequently cured in a forced air oven at 160° C. for 30minutes.

The results are found in table 2. The waterborne basecoat material (WBM)detail indicates which WBM was used in the particular multicoat paintsystem.

TABLE 2 Stonechip resistance of the waterborne basecoat materials 2 andI3, I4 WBM Stonechip result  2 + 3 2.5 I3 + 3 1.5 I4 + 3 1.5

The results emphasize again that the use of the inventive reactionproducts in basecoat materials increases the stonechip resistance bycomparison with non-inventive systems.

1. A pigmented aqueous basecoat material comprising a hydroxy-functionalpolyether-based reaction product that is preparable by urethanegroup-forming reaction of: (a) at least one component containingisocyanate groups that is preparable by urethane group-forming reactionof at least one organic diisocyanate (a1) with at least one polyether(a2) of the general structural formula (I),

wherein R is a C₃ to C₆ alkylene radical, and n is selected accordinglysuch that the polyether (a2) possesses a number-average molecular weightof 500 to 5000 g/mol, wherein the components (a1) and (a2) are used in amolar ratio of 1.8/1.7 to 3.0/1.0, and a resulting component (a) has anisocyanate content of 0.5 to 10%, with (b) at least one organic polyol,wherein the amounts of components (a) and (b) are harmonized with oneanother such that the ratio of the molar amount of isocyanate groups incomponent (a) to the molar amount of component (b) is in a range from0.33 to 0.95, and the resulting reaction product has a number-averagemolecular weight of 700 to 20,000 g/mol.
 2. The pigmented aqueousbasecoat material as claimed in claim 1, wherein the polyether (a2)possesses a number-average molecular weight of 600 to 3,200 g/mol. 3.The pigmented aqueous basecoat material as claimed in claim 1, whereinthe group R in the general structural formula (I) comprisestetramethylene radicals.
 4. The pigmented aqueous basecoat material asclaimed in claim 1, wherein the amounts of components (a) and (b) areharmonized with one another in such a way that the ratio of the molaramount of isocyanate groups in component (a) to the molar amount ofcomponent (b) is in a range from 0.40 to 0.85.
 5. The pigmented aqueousbasecoat material as claimed in claim 1, wherein the polyether-basedreaction product possesses a number-average molecular weight of 1,500 to12,000 g/mol.
 6. The pigmented aqueous basecoat material as claimed inclaim 1, wherein component (a) has an isocyanate content of 1.0 to 6.5%.7. The pigmented aqueous basecoat material as claimed in claim 1,wherein the sum total of the weight-percentage fractions, based on thetotal weight of the pigmented aqueous basecoat material, of allpolyether-based reaction products is 0.1 to 20 wt %.
 8. The pigmentedaqueous basecoat material as claimed in claim 1, further comprising amelamine resin and also a polyurethane resin that is grafted by means ofolefinically unsaturated monomers and that further comprises hydroxylgroups.
 9. The pigmented aqueous basecoat material as claimed in claim1, wherein the component (b) has three hydroxyl groups.
 10. Ahydroxy-functional polyether-based reaction product that is preparableby urethane group-forming reaction of: (a) at least one componentcontaining isocyanate groups that is preparable by urethanegroup-forming reaction of at least one organic diisocyanate (a1) with atleast one polyether (a2) of the general structural formula (I),

wherein R is a C₃ to C₆ alkylene radical, and n is selected accordinglysuch that the polyether (a2) possesses a number-average molecular weightof 500 to 5,000 g/mol, wherein the components (a1) and (a2) are used ina molar ratio of 1.8/1.7 to 3.0/1.0, and a resulting component (a) hasan isocyanate content of 0.5 to 10.0%, with (b) at least one organicpolyol, wherein the amounts of components (a) and (b) are harmonizedwith one another such that the ratio of the molar amount of isocyanategroups in component (a) to the molar amount of component (b) is in arange from 0.33 to 0.95, and the resulting reaction product has anumber-average molecular weight of 700 to 20,000 g/mol.
 11. A method ofusing the reaction product as claimed in claim 10, the method comprisingusing the reaction product in a pigmented aqueous basecoat material forimproving the stonechip resistance of paint systems produced using thebasecoat material.
 12. A method for producing a multicoat paint systemby: (1) applying a pigmented aqueous basecoat material to a substrate,(2) forming a polymer film from the coating material applied in stage(1), (3) applying a clearcoat material to the resultant basecoat, andsubsequently (4) curing the basecoat together with the clearcoat,wherein the pigmented aqueous basecoat material as claimed in claim 1 isused in step (1).
 13. The method as claimed in claim 12, wherein thesubstrate from stage (1) is a metallic substrate coated with a curedelectrocoat, and all coats applied to the electrocoat are cured jointly.14. The method as claimed in claim 12, wherein the substrate from stage(1) is a metallic or plastics substrate.
 15. A multicoat paint systemproducible by the method as claimed in claim 12.